CHOSERICERCAPUBBLICAZIONIPOLYMER/INORGANIC HOLE TRANSPORT LAYER FOR LOW-TEMPERATURE-PROCESSED PEROVSKITE SOLAR CELLS

POLYMER/INORGANIC HOLE TRANSPORT LAYER FOR LOW-TEMPERATURE-PROCESSED PEROVSKITE SOLAR CELLS

P3HTCuSCN 1

ABSTRACT

In the work we introduce a hysteresis-free low-temperature planar PSC, composed of a poly (3-hexylthiophene)(P3HT)/CuSCN bilayer as a hole transport layer (HTL) and a mixed cation perovskite absorber. Proper adjustment of the precursor concentration and thickness of the HTL led to a homogeneous and dense HTL on the perovskite layer. This strategy not only eliminated the hysteresis of the photocurrent, but also permitted power conversion efficiencies exceeding 15.3%. The P3HT/CuSCN bilayer strategy markedly improved the life span and stability of the non-encapsulated PSCs under atmospheric conditions and accelerated thermal stress. The device retained more than 80% of its initial efficiency after 100 h (60% after 500 h) of continuous thermal stress under ambient conditions.

Authors:

Neda Irannejad, Narges Yaghoobi Nia, Siavash Adhami, Enrico Lamanna, Behzad Rezaei, Aldo Di Carlo

https://doi.org/10.3390/en13082059

MDPI Journals Energies Vol. 13 Issue 8

https://www.mdpi.com/1996-1073/13/8/2059

 

 

logo University of Rome Tor Vergata
Università degli Studi di Roma
"Tor Vergata"


logo Regione Lazio

Questo sito web utilizza i cookie per capire come viene utilizzato il sito e per permettere l'accesso all'area riservata. I cookie non permettono di identificare l'utente. I cookie sono salvati sul tuo browser e sono utlizzati per personalizzare la tua esperienza sul nostro sito web. Continuando la navigazione sul nostro sito senza modificare le impostazioni, accetti il nostro utilizzo dei cookie. Comunque potrai modificare le tue impostazioni dei cookie in qualsiasi momento.