To improve the efficiency of perovskite solar cells, careful device design and tailored interface engineering are needed to enhance optoelectronic properties and the charge extraction process at the selective electrodes. Here, we use two-dimensional transition metal carbides (MXene Ti3C2Tx) with various termination groups (Tx) to tune the work function (WF) of the perovskite absorber and the TiO2 electron transport layer (ETL), and to engineer the perovskite/ETL interface. Ultraviolet photoemission spectroscopy measurements and density functional theory calculations show that the addition of Ti3C2Tx to halide perovskite and TiO2 layers permits the tuning of the materials’ WFs without affecting other electronic properties. Moreover, the dipole induced by the Ti3C2Tx at the perovskite/ETL interface can be used to change the band alignment between these layers. The combined action of WF tuning and interface engineering can lead to substantial performance improvements in MXene-modified perovskite solar cells, as shown by the 26% increase of power conversion efficiency and hysteresis reduction with respect to reference cells without MXene.

A. Agresti, A. Pazniak, S. Pescetelli, A. Di Vito, D. Rossi, A. Pecchia, M. Auf der Maur, A. Liedl, R. Larciprete, Denis V. Kuznetsov, D. Saranin, A. Di Carlo

Nature Materials, 09 September 2019



logo University of Rome Tor Vergata
Università degli Studi di Roma
"Tor Vergata"

logo Regione Lazio

Questo sito web utilizza i cookie per capire come viene utilizzato il sito e per permettere l'accesso all'area riservata. I cookie non permettono di identificare l'utente. I cookie sono salvati sul tuo browser e sono utlizzati per personalizzare la tua esperienza sul nostro sito web. Continuando la navigazione sul nostro sito senza modificare le impostazioni, accetti il nostro utilizzo dei cookie. Comunque potrai modificare le tue impostazioni dei cookie in qualsiasi momento.