FACILE SYNTHESIS OF A SNO2@RGO NANOHYBRID AND OPTIMIZATION OF ITS METHANE-SENSING PARAMETERS

 

stannic oxide nanoparticles1

 

ABSTRACT

Stannic oxide nanoparticles and various compositions of SnO2@rGO (reduced graphene oxide) nanohybrids were synthesized by a facile hydrothermal method and utilized as chemiresistive methane gas sensors. To characterize the synthesized nanohybrids, BET (Brunauer-Emmett-Teller), XRD, FESEM, TEM, FTIR, and Raman techniques were used. Sensing elements were tested using a U-tube flow chamber with temperature control. To obtain the best sensor performance, i.e., the highest signal and the fastest response and recovery times, the sensing element composition, operating temperature, and gas flow rate were optimized. The highest response (change in resistance) of 47.6% for 1000 ± 5 ppm methane was obtained with the SnO2@rGO1% nanohybrid at 150 °C and a flow rate of 160 sccm; the response and recovery times were 61 s and 5 min, respectively. A sensing mechanism was suggested, based on the experiments.

Shiva Navazani, Ali Shokuhfar, Mostafa Hassanisadi, Mojtaba Askarieh, Aldo Di Carlo, Antonio Agresti

DOI: 10.1016/j.talanta.2018.01.015

https://www.sciencedirect.com/science/article/pii/S0039914018300213

 

 

logo University of Rome Tor Vergata
Università degli Studi di Roma
"Tor Vergata"


logo Regione Lazio

Questo sito web utilizza i cookie per capire come viene utilizzato il sito e per permettere l'accesso all'area riservata. I cookie non permettono di identificare l'utente. I cookie sono salvati sul tuo browser e sono utlizzati per personalizzare la tua esperienza sul nostro sito web. Continuando la navigazione sul nostro sito senza modificare le impostazioni, accetti il nostro utilizzo dei cookie. Comunque potrai modificare le tue impostazioni dei cookie in qualsiasi momento.